Tensile and Tear Resistance Tests for Fabrics

Tear Resistance Test

The Tear Resistance test measures the force required to tear a sample material such as woven or nonwoven fabrics and plastic film or sheeting. This test allows manufacturers to determine the strength of the sample.

This test complies with the following standards: ASTM D1004 Standard Test Method for Initial Tear Resistance of Plastic Film and Sheeting, and ASTM D5587 Standard Test Method for Tearing Strength of Fabrics by Trapezoid procedure. Nelson Labs is an active member of ASTM committees.

Tensile Testing

Tensile testing measures the force needed to elongate and break a sample. It is used to determine the strength and elasticity of woven or nonwoven fabrics, plastic film or sheeting, gloves, condoms and other materials.

Nelson Labs tests fabrics by EN 29073 or ISO 9073, or ASTM D5034 and D5035. Plastics are tested according to ASTM D882, ASTM D638. Fabrics are tested wet or dry. We are an active member of ASTM committees.

For tests specific to surgical gowns and drapes, please see:

Applicable Standards

  • NFPA 1999
  • ASTM D5034
  • ASTM D5035
  • ASTM D882
  • ASTM D638
  • ISO 9073
  • EN 13795
  • EN 29073

Testing Locations

  • Salt Lake City, UT, USA

Learn more about our locations and their certifications.

Study Outline

Tear Resistance

In the Tear Resistance test, plastic samples are cut using the ASTM D1004 C die and the average of several thickness measurements is reported. The instrument is set up with the crosshead speed to 2 inches per minute and the specimen is inserted into the grips. The maximum load in pound force for the specimen is reported.

Fabric samples are cut to 3 x 6 inches. The instrument is set to 12 inches per minute and the specimen is inserted into the grips. The maximum load in pound force is reported.

Puncture GLU 140 is also used for fabrics and plastic films.

Tensile Testing

Thin plastic films are tested by cutting a ½ inch wide strip.  Thickness is measured at three locations. The speed and grip distances vary depending on the % elongation of the sample.  Samples are pulled until break, and the breaking factor, tensile strength, tensile at break, elongation and modulus are reported.

Thicker plastics are cut with the ASTM D412 die C. Marks are made 1 inch apart and the median of three thickness measurements is used in calculating the cross-sectional area. The instrument is set up with the crosshead speed to 20 inches per minute and the specimen is inserted into the grips. The elongation of the specimen is measured between the marks with an extensometer.

Fabric samples are cut to 4 x 6 inches in both the machine and cross directions. The instrument is set to 12 inches per minute and the specimen is inserted into the 1 x 1 inch grips.  The sample is pulled until break, and the breaking force and elongation are measured.

Puncture GLU 140 is also used for fabrics and plastic films.

If you have additional questions about Tensile and Tear Resistance testing, or would like to consult with the experts at Nelson Labs, just send us a request or call us at +1 (801) 290-7500.